1. Identificação | |
Tipo de Referência | Artigo em Revista Científica (Journal Article) |
Site | mtc-m16b.sid.inpe.br |
Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S |
Identificador | 6qtX3pFwXQZGivnK2Y/S9iNq |
Repositório | sid.inpe.br/mtc-m17@80/2007/11.13.12.51 (acesso restrito) |
Última Atualização | 2007:11.13.12.51.33 (UTC) administrator |
Repositório de Metadados | sid.inpe.br/mtc-m17@80/2007/11.13.12.51.34 |
Última Atualização dos Metadados | 2018:06.05.03.35.01 (UTC) administrator |
Chave Secundária | INPE-14899-PRE/9813 |
ISSN | 0257-8972 |
Chave de Citação | SilvaUedaSilvCoda:2007:CoBeTi |
Título | Corrosion behavior of Ti-6Al-4V alloy treated by plasma immersion ion implantation process |
Ano | 2007 |
Mês | Aug. |
Data de Acesso | 18 maio 2024 |
Tipo Secundário | PRE PI |
Número de Arquivos | 1 |
Tamanho | 777 KiB |
|
2. Contextualização | |
Autor | 1 Silva, Leide Lili Gonçalves da 2 Ueda, Mário 3 Silva, M. M. 4 Codaro, E. N. |
Grupo | 1 LAP-INPE-MCT-BR 2 LAP-INPE-MCT-BR |
Afiliação | 1 Instituto Nacional de Pesquisas Espaciais (INPE) 2 Instituto Nacional de Pesquisas Espaciais (INPE) 3 Department of Mechanical Engineering, Technological Institute of Aeronautics (ITA) 4 Faculdade de Engenharia de Guaratinguetá. Universidade Estadual Paulista (FEG.UNESP) |
Endereço de e-Mail do Autor | 1 leide@plasma.inpe.br |
Revista | Surface and Coatings Technology |
Volume | 201 |
Número | 19/20 |
Páginas | 8136-8139 |
Histórico (UTC) | 2007-11-13 13:03:02 :: simone -> administrator :: 2008-06-29 02:36:49 :: administrator -> simone :: 2011-05-29 09:47:36 :: simone -> administrator :: 2012-10-23 23:58:43 :: administrator -> simone :: 2007 2013-02-20 15:20:02 :: simone -> administrator :: 2007 2018-06-05 03:35:01 :: administrator -> marciana :: 2007 |
|
3. Conteúdo e estrutura | |
É a matriz ou uma cópia? | é a matriz |
Estágio do Conteúdo | concluido |
Transferível | 1 |
Tipo do Conteúdo | External Contribution |
Palavras-Chave | Ti-6Al-4V alloy plasma immersion ion implantation corrosion nitride layer TITANIUM RESISTANCE FILMS OXIDE |
Resumo | Ti-6Al-4V alloy is one of the most frequently used Ti alloys with diverse applications in aerospace and biomedical areas due to its favorable mechanical properties, corrosion resistance and biocompatibility. Meanwhile, its surface can stiffer intense corrosion caused by wear processes due to its poor tribological properties. Thus in the present study, PIII processing of Ti-6Al-4V alloy was carried out to evaluate its corrosion resistance in 3.5% NaCl solution. Two different sets of Ti-6Al-4V samples were PIII treated, varying the plasma gases and the treatment time. The corrosion behavior is correlated with the surface morphology, and the nitrogen content. SEM micrographs of the untreated sample reveal a typical two-phase structure. PIII processing promotes surface sputtering and the surface morphology is completely different for samples treated with N-2/H-2 mixture and N-2 only. The highest penetration of nitrogen (similar to 88 nm), corresponding to 33% of N-2 was obtained for the sample treated with N-2/H-2 mixture for 1:30 h. The corrosion behavior of the samples was investigated by a potentiodynamic polarization method. A large passive region of the polarization curves (similar to 1.5 V), associated with the formation of a protective film, was observed for all samples. The passive current density (similar to 3 x 10(-6) A cm(-2)) of the PIII-treated Ti-6Al-4V samples is about 10 times higher than for the untreated sample. This current value is still rather low and maintains good corrosion resistance. The anodic branches of the polarization curves for all treated Ti-6Al-4V samples demonstrate also that the oxide films break down at approximately 1.6 V, forming an active region. Although the sample treated by N-2/H-2 mixture for 1.30 It has thicker nitrogen enriched layer, better corrosion resistance is obtained for the PIII process performed with N, gas only. |
Área | FISPLASMA |
Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAP > Corrosion behavior of... |
Conteúdo da Pasta doc | acessar |
Conteúdo da Pasta source | não têm arquivos |
Conteúdo da Pasta agreement | não têm arquivos |
|
4. Condições de acesso e uso | |
Idioma | en |
Arquivo Alvo | corrosion beharvior of ti 6al 4v alloy.pdf |
Grupo de Usuários | administrator simone |
Visibilidade | shown |
Detentor da Cópia | SID/SCD |
Política de Arquivamento | denypublisher denyfinaldraft24 |
Permissão de Leitura | deny from all and allow from 150.163 |
|
5. Fontes relacionadas | |
Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ET2RFS |
Divulgação | WEBSCI; PORTALCAPES. |
Acervo Hospedeiro | lcp.inpe.br/ignes/2004/02.12.18.39 cptec.inpe.br/walmeida/2003/04.25.17.12 |
|
6. Notas | |
Campos Vazios | alternatejournal archivist callnumber copyright creatorhistory descriptionlevel documentstage doi e-mailaddress format isbn label lineage mark mirrorrepository nextedition notes orcid parameterlist parentrepositories previousedition previouslowerunit progress project readergroup resumeid rightsholder schedulinginformation secondarydate secondarymark session shorttitle sponsor subject tertiarymark tertiarytype typeofwork url versiontype |
|
7. Controle da descrição | |
e-Mail (login) | marciana |
atualizar | |
|